This study aims to enhance the corrosion property of 17-4PH martensitic stainless steel, a material commonly used in industrial applications including nuclear power components, to enhance its performance in borate buffer solutions. The study employed plasma-based low-energy nitrogen ion implantation at temperatures ranging from 350 °C to 550 °C for 4 h to modify the steel surface. Microstructural characterization via XRD and TEM revealed the formation of a nanocrystalline nitrided layer, with thickness increasing from 11 to 27 μm and surface nitrogen concentration rising from 29.7 to 33.1% as temperature increased. Correspondingly, the nanocrystalline grains coarsened from an average size of 2 nm to 15 nm. The main findings showed that all nitrided layers significantly improved general corrosion resistance in pH 8.4 borate solution compared to the unmodified steel. An optimal performance with a corrosion potential of −169.4 mV(SCE) and a passive current density of 0.5 μA/cm2 was achieved at 450 °C, accompanying the development of a denser passive film with high polarization resistance and lower defect density. It is concluded that the high interstitial nitrogen concentration within the nanocrystalline γ′N accelerates passivation kinetics and enhances corrosion resistance, with the applied point defect model clarifying the underlying improvement mechanism.