Effect of Annealing Atmosphere on the Microstructure and High-Frequency Magnetic Properties of FeSiCr Soft Magnetic Composites

Annealing is a critical step in the fabrication of soft magnetic composites (SMCs), and precise coordination of annealing atmosphere and temperature is essential for optimizing their performance. In this study, FeSiCr SMCs were annealed under three different atmospheres (air, nitrogen, and argon) across a range of temperatures, and the effects of the annealing atmosphere on their microstructure and soft magnetic properties were systematically investigated. The results demonstrate that annealing in an inert atmosphere, particularly argon, within the temperature range of 450–750 °C, yields superior magnetic properties compared with air annealing. After annealing under argon at 550 °C, the effective magnetic permeability (μe) reached 47.5, and the power loss (Pcv) was 1457.3 kW/m3 at 1000 kHz and 30 mT. These improvements are primarily attributed to effective stress relaxation and the substantial retention of the polyvinyl butyral (PVB) insulating layer. With further increases in annealing temperature, the magnetic properties deteriorate rapidly due to the complete decomposition of PVB and the formation of conductive chromium carbides. Under such conditions, air annealing exhibits distinct advantages. Selective oxidation of FeSiCr occurs, leading to the formation of a dense chromium oxide insulating layer that enhances magnetic performance (after annealing at 850 °C, μe = 47.9, Pcv = 1632.0 kW/m3). Moreover, the mechanical properties were significantly improved, with the radial crush strength increasing from 22.36 N in the unannealed state to 330 N after annealing. These results indicate that the comprehensive performance of SMCs can be effectively tailored through the appropriate selection of annealing atmosphere and temperature, providing valuable guidance for the design and optimization of high-performance SMCs.