Microstructure Evolution and Mechanical Properties of Al0.5Cr0.9FeNi2.5V0.2 High-Entropy Alloy Fabricated by Binder Jetting 3D Printing and Vacuum Sintering

Dezhi Zhu, Jinchuan Peng, Yongchi Wu, Xiaohui Qin, Xiaodong Wang, Qi Yang, Xi Huang, Guanghui Xu, Erlei Li

原始摘要(英文原文)· Original abstract
Binder Jetting 3D Printing (BJ3DP) offers an effective pathway for the rapid fabrication of complex high-entropy alloy (HEA) components. In this study, the macroscopic characteristics, microstructural evolution and mechanical properties of Al0.5Cr0.9FeNi2.5V0.2 HEA green parts prepared via BJ3DP were investigated under various sintering conditions. Results showed that the relative density of the sintered parts increased significantly with temperature, transitioning from a low density (<90%) at 1300–1330 °C to near-fully dense (~98%) at 1340–1350 °C. Consequently, the mechanical properties were remarkably improved. The yield strength (σ0.2) increased from 300 MPa to 710 MPa (a 136% increase), and the ultimate tensile strength (σb) rose from 310 MPa to 780 MPa (a 148% increase) as sintering temperature rose from 1300 °C to 1350 °C. Microstructural analysis revealed that at lower sintering temperatures, the alloy exhibited high porosity and a non-coherent structure composed of an FCC matrix and Cr-rich BCC phase, with Al/Ni intermetallic compounds distributed around pores. Conversely, at the final sintering stage, pore closure was achieved, and a coherent structure consisting of an FCC matrix and scale-like L12 precipitates was formed. Optimal mechanical properties (tensile strength ≥ 700 MPa) were achieved when sintering at 1340 °C, primarily attributed to densification and precipitation strengthening.
读原文 · Read the paper ↗

AI 追问PRO

登录后使用 AI 追问

讨论区

登录后参与讨论

相关论文 · Related

Microstructure Evolution and Mechanical Properties of Al0.5Cr0.9FeNi2.5V0.2 High-Entropy Alloy Fabricated by Binder Jetting 3D Printing and Vacuum Sintering — 科研速览 Science Skim