Solidification cracking of laser melted commercial-purity tungsten

The high melting temperature of tungsten (W) makes it an attractive candidate for energy generation applications; however, its use is limited by its poor ductility at low temperatures. This limitation affects even melt-based additive manufacturing (AM) processes such as laser powder bed fusion (PBF-LB), with as-fabricated pure W exhibiting both longitudinal and transverse cracks. Metallurgical and processing factors that affect these cracks are still being explored. This work utilizes powderless single-tracks on pure W plates made over a range of power and velocity combinations in three unique PBF-LB setups: one with flowing argon, one with continuous vacuum, and an in situ high-speed synchrotron X-ray radiography setup. Each had different oxygen activities in their build environments. Longitudinal cracks with oxides appearing to exude from the crack were found for tracks deposited in a build environment with argon shield gas, while no such cracks were observed for builds conducted in vacuum. A calculation showed that direct oxygen ingress into the melt pool from the build environment is negligible when argon shield gas is present. Thus, incorporation of spatter is a likely mechanism for oxygen ingress into the melt pool. Radiography showed extensive keyholing, spatter generation, and crack formation at keyhole porosity. A heat transfer calculation showed the crack formation time was consistent with cooling below its ductile-to-brittle transition (DBT) temperature. This work identifies solidification cracking as a feasible mechanism in pure W beyond the well-known DBT related cracking.