Production of Chromium–Manganese Ligature from Low-Grade Chromium and Iron–Manganese Ores Using Silicon–Aluminum Alloys as Reductants

This study investigates the production of chromium–manganese ligature by a metallothermic process using complex silicon–aluminum reducing agents. Low-grade chromium and iron–manganese ores from the Kempirsai and Kerege-Tas deposits in Kazakhstan were used as raw materials, while the reducing agents included alumosilicomanganese alloy (AlSiMn) and ferrosilicoaluminum (FeSiAl). Thermodynamic calculations were performed with HSC Chemistry 10 at 1400–1800 °C and reducing agent dosages of 10–100 kg per 100 kg of ore charge. Crucible smelting experiments were then carried out in a Tamman furnace, followed by large-scale laboratory trials in a 100 kVA refining electric furnace to verify reproducibility, with a total of 14 runs. The chemical composition of the ligatures varied depending on the reductant: with AlSiMn the alloy contained Fe—23.14%, Cr—53.74%, Mn—20.03%, and Si—3.06%; with FeSiAl, it contained Fe—42.01%, Cr—25.74%, Mn—27.15%, and Si—5.05%; and with FeSiCr dust, it contained Fe—34.45%, Cr—21.45%, Mn—39.82%, and Si—4.24%. X-ray diffraction (XRD) and scanning electron microscopy (SEM) analyses confirmed the presence of α-(Fe,Cr,Mn), FeSi, and Cr5Si3 phases. The results demonstrate the efficiency of complex silicon–aluminum reducing agents and the ability to regulate the composition of chromium–manganese ligatures by the selected reductant.