The simulation of solidification microstructures of cast alloys is crucial to the integrated “process–microstructure–property” numerical simulation. In order to verify the accuracy of the solidification microstructure simulation results, the solidification microstructures of WE54 alloy under both metal mold casting (MMC) and sand mold casting (SMC) conditions were simulated using the CAFE (Cellular Automaton–Finite Element) method, and the simulation results were validated experimentally. First, the effects of microstructure simulation parameters on the results were investigated, including nucleation density (n), nucleation undercooling (ΔT), and dendrite tip growth kinetics parameters (a2, a3). The results showed that, with the maximum surface nucleation undercooling (ΔTs,max) kept constant, increasing the maximum volume nucleation undercooling (ΔTv,max) significantly increases the proportion of columnar grains in the ingot structure. Moreover, when nucleation parameters remain constant, increasing a2 and a3 leads to expansion of the columnar grain zone. Secondly, numerical simulations of the solidification microstructure of WE54 alloy under different solidification conditions were carried out. The results indicated that as the cooling rate increases, the grain structure of the ingot becomes significantly refined, and the proportion of columnar grains decreases notably. Based on these findings, the simulation parameters suitable for simulating the solidification process and microstructure of MMC and SMC WE54 alloy were determined. Simulations of the temperature field and solidification microstructure were performed and compared with experimental results.