Fe24Ni15Cr3Al-Based AFA Steels in Oxygen-Controlled Liquid Pb at 500 °C, 600 °C, and 700 °C.

Heavy liquid metals such as liquid lead (Pb) are attractive heat transfer media for advanced energy applications, despite their corrosive nature. In the search for heat-resistant austenitic materials that are corrosion resistant to liquid Pb at high temperature, three new Fe24Ni15Cr3Al-based alumina-forming austenitic (AFA) steels with slightly varying compositions have been developed. The present study investigates the corrosion behavior of these AFA materials using static exposure tests to molten Pb containing 1 × 10-7 wt.% dissolved oxygen. The corrosion tests are performed at 500 °C, 600 °C, and 700 °C for 1000 h, 2000 h, and 5000 h each. In addition to the variation in material, temperature, and exposure time, two different surface finishes are also used for the tests. Examination of the specimens after exposure shows the formation of oxide scales for temperatures up to 600 °C on all three AFA materials, with minor material-specific variations. Furthermore, the scale characteristics depend on the surface finish. Coarse ground surfaces exhibit thin Al-rich protective oxide scales, while fine ground surfaces show the formation of thick multilayer oxide scales susceptible to Ni dissolution and Pb penetration. Pb exposure at 700 °C leads to a severe corrosion attack of all three Fe24Ni15Cr3Al-based AFA steels.