Xinjie Zhao, Lei He, Yi Xu, Guodong Li
In view of the fact that there are few reports on the preparation of NbC coating by high-power pulsed magnetron sputtering (HiPIMS) technology. In this study, the effects of NbC interlayer thickness on the microstructure, corrosion resistance and electrical conductivity of Nb/NbC/C multilayer coatings for proton exchange membrane fuel cell (PEMFC) bipolar plates were studied by using the high ionization characteristics of HiPIMS technology. A series of Nb/NbC/C multilayer coatings with varying NbC interlayer thicknesses was deposited via HiPIMS by modulating the deposition time (20, 40, and 60 min). The microstructure and properties of the coatings were characterized using scanning electron microscopy (SEM), Raman spectroscopy, interfacial contact resistance (ICR), and corrosion current, among other methods. The results indicate that as the NbC interlayer thickness increases, the total coating thickness increases from 0.43 μm to 1.42 μm. All coatings exhibit a uniform and dense microstructure lacking typical coarse columnar structures. Raman and XPS analyses show that the ID/IG ratio increases from 1.98 to 4.04, indicating an increase in sp2-hybridized bond content and a decrease in sp3 content. At a deposition time of 60 min, the coating achieved optimal performance, yielding a critical load (Lc1) of 31.9 N, the lowest average friction coefficient (0.27), the minimum corrosion current density, and an interfacial contact resistance of 7.5 mΩ·cm2. These results demonstrate that the NbC interlayer thickness significantly governs the structure and properties of the Nb/NbC/C multilayer coatings. Specifically, an appropriate increase in the NbC interlayer thickness optimizes the sp2/sp3 hybrid bond ratio, thereby enhancing the overall coating performance.