Melting point of group IV and V transition metal diborides

Abstract The environmental conical nozzle levitator system enables cooling trace experiments above 4000 K. These cooling trace experiments were used to determine the melting points through observation of thermal arrest of group IV and V transition metal diborides (TiB 2 , T m = 3313 ± 33 K; ZrB 2 , T m = 3404 ± 38 K; HfB 2 , T m = 3529 ± 33 K; and TaB 2 , T m = 3284 ± 10 K; note: mean ± 2 standard error). Temperature measurements were conducted utilizing dual single‐color pyrometers at wavelengths of 0.9 and 0.65 µm. This system utilizes aerodynamic levitation and dual laser heating to achieve temperatures approaching 4000 K. The samples were synthesized from commercial powders using ceramic gel‐casting to produce high‐density spherical components. The measurements obtained were compared to previously reported melting temperature values and were generally found to be in agreement with most of the published values.