In Situ Imaging Reveals Efficient Charge Separation in Monolayer MoS ₂ –WS ₂ Type-II Heterojunctions

High Resolution Image Download MS PowerPoint Slide Covalently bonded in-plane two-dimensional (2D) transition metal dichalcogenide (TMD) heterojunctions with atomically sharp interfaces hold great promise for photocatalytic applications in solar energy conversion and environmental remediation; however, their spatially resolved charge distribution and transport, particularly under operando conditions, remain poorly understood. Here, we employ photoscanning electrochemical microscopy (photo-SECM) to directly visualize photoinduced charge separation in monolayer MoS 2 –WS 2 in-plane heterojunctions. Spatial separation of photogenerated carriers is observed, with electrons accumulating in MoS 2 and holes in WS 2, leading to strongly asymmetric interfacial kinetics: Fc + reduction proceeds rapidly on MoS 2 (0.6 cm s –1 ), whereas Fc oxidation on WS 2 is significantly slower (0.008 cm s –1 ). High-resolution surface photovoltage microscopy (SPVM) enables a quantitative comparison of charge-separation capacity across architectures. The in-plane MoS 2 –WS 2 heterojunction shows the largest photovoltage contrast (−35 mV in MoS 2, 20 mV in WS 2 ), exceeding the vertical heterojunction (−18 mV in MoS 2, 11 mV in WS 2 ) and the individual monolayers (−12 mV for MoS 2, – 1 mV for WS 2 ), establishing the following trend: in-plane > vertical > monolayers. Ultraviolet photoelectron spectroscopy (UPS) indicates that this directional charge separation is driven by intrinsic type-II band alignment, while photoluminescence (PL) imaging shows that the interface acts as a recombination center that limits efficient carrier extraction. These results provide direct experimental evidence of type-II-driven charge separation in in-plane heterojunctions and offer critical insights for interface design in high-efficiency photocatalytic and optoelectronic systems.