Yiliang Chen, Yuzhuo Bai, Shaoqiu Ke, Shaoqiu Ke, Xiaohuan Wei, X B Zhang, Xiaojia Xu, Zhiming Li, Bin Liu, Zhiwei Huang, Guanzhou Liu, Jinrong Zhou, Zhen Wang, Shaoying Ke, Shaoying Ke
Two-dimensional (2D) PtTe 2 films with controlled crystallinity and morphology are synthesized via a dual-zone temperature modulation strategy, enabling tailored growth of low-roughness single-oriented (LRSO, denoting uniaxial preferred orientation), medium-roughness multioriented (MRMO), and high-roughness multioriented (HRMO) PtTe 2 . Systematic characterization reveals distinct structural features: LRSO-PtTe 2 exhibits high crystallographic alignment (RMS roughness: 3.9 nm), while HRMO-PtTe 2 displays disordered orientations and elevated roughness (55.9 nm), which is attributed to Te-deficient growth under high-temperature conditions. Leveraging these materials, PtTe 2 /Ge heterojunction photodetectors are fabricated, demonstrating broadband detection from visible (532 nm) to mid-infrared (4156 nm). The HRMO-PtTe 2 /Ge device achieves responsivity (228 mA W –1 at 1550 nm) and specific detectivity (2.26 × 10 11 Jones), outperforming LRSO-PtTe 2 /Ge counterparts due to enhanced light scattering and interfacial strain relaxation. Remarkably, the LRSO-PtTe 2 /Ge device exhibits fast response speeds (rise/fall time: 0.84/8.27 μs) and a high 3 dB bandwidth of 0.272 MHz, attributed to its defect-minimized crystalline structure. Both devices enable high-fidelity grayscale imaging via single-pixel mapping, validated under 1550 nm illumination. This work elucidates the interplay between growth kinetics and optoelectronic performance, advancing the development of high-speed, broadband photodetectors for imaging and sensing applications.