Effect of Heat Input on Interface Microstructure and Mechanical Properties of Al/Cu Laser Lap Welded Joints for Medium-Thickness Plates.

To meet the demands for lightweight design and high-conductivity connections in new energy vehicles, the high-quality joining of dissimilar Al/Cu metals has emerged as a critical research focus. In this study, laser welding was performed on 2 mm-thick 1060 pure aluminum and T2 copper plates. The effects of laser power (3.6-4.0 kW) and welding speed (0.9-1.5 m/min) on the interfacial microstructural evolution and mechanical properties of the lap joints were systematically investigated. The results demonstrate that the macroscopic morphology of the weld is primarily governed by heat input: excessive laser power induces transverse cracking, whereas an overly low welding speed promotes porosity. Microstructural analysis revealed that intermetallic compounds (IMCs), such as Al2Cu, AlCu, and Al4Cu9, predominantly form at the interface, with their morphology and distribution varying significantly depending on the heat input. Under the optimized parameters of a 3.8 kW laser power and a 1.2 m/min welding speed, sufficient mixing of the molten Al and Cu was achieved. This promoted the formation of fine, dispersed IMCs accompanied by a continuous Al-Cu eutectic layer at the interface, yielding a maximum tensile-shear load of 1561 N. This research elucidates the intrinsic relationship between heat input and the microstructure-property correlation of Al/Cu laser-welded joints, identifying a viable process window for 2 mm-thick sheets and providing theoretical and practical guidance for joining dissimilar medium-thickness metal plates.