Wenjing Chang, Jingyi Hang, Xiaoxing Yan
Thermochromic wood coatings hold promising application prospects, yet conventional thermochromic microcapsules are limited by monotonous color transitions and non-environmentally friendly wall materials. In this study, two formaldehyde-free thermochromic microcapsules were prepared via spray drying using crystal violet lactone (CVL) and bisphenol A (BPA) as the core system, with chitosan-syringaldehyde (SA-MCs, decyl alcohol as solvent, Schiff base crosslinking) and chitosan-gum Arabic (GA-MCs, lauryl alcohol as solvent, electrostatic complex coacervation) as the wall materials, respectively. These microcapsules were incorporated into basswood ultraviolet (UV) coatings at mass fractions of 1%, 3%, 5%, 7%, and 9%. With increasing microcapsule content, the gloss of both coatings decreased progressively, roughness increased gradually, and the color-changing amplitude, expressed as the color difference (ΔE), was continuously enhanced. At 9% addition, the SA-MC coating exhibited a moderate transition from light yellow to yellow-green (ΔE = 7.2), while the GA-MC coating displayed a dramatic reversible change from deep blue to light gray (ΔE = 42.4), both with good reversibility. In terms of mechanical properties, SA-MCs exhibited higher hardness, both systems achieved an impact resistance grade of 3, and GA-MCs demonstrated superior adhesion. After 24 h of short-term UV accelerated aging, GA-MCs still maintained a higher thermochromic response, albeit with more severe gloss loss. In summary, GA-MCs are superior in color-changing amplitude and adhesion, while SA-MCs offer advantages in gloss retention and hardness, providing a reference for material selection in the application of smart wood finishing.